Product Introduction
1.Overview
This PBT Glass Fiber Reinforced Compound is a high-performance engineering thermoplastic designed for applications requiring excellent mechanical strength, rigidity, and dimensional stability. With 20% to 30% glass fiber content, this grade offers superior heat resistance and creep resistance compared to unfilled PBT. It is a non-flame retardant (General Purpose) grade, ideal for applications where flame retardancy is not required.
2.Key Features
High Strength & Stiffness – Reinforced with 20%-30% glass fiber for enhanced mechanical properties.
Excellent Heat Resistance – High heat deflection temperature (HDT) suitable for under-hood and high-temperature environments.
Good Dimensional Stability – Low moisture absorption, minimal warpage, and excellent part-to-part consistency.
Chemical Resistance – Resists oils, greases, and many solvents.
Non-FR Grade – Cost-effective solution for general industrial applications without flame retardant additives.
Easy Processing – Suitable for injection molding with good flowability.
3.Technical Data Sheet
| Property | Unit | Value (PBT GF20) | Value (PBT GF30) |
| Glass Fiber Content | % | 20 | 30 |
| Tensile Strength | MPa | 110 | 135 |
| Flexural Modulus | MPa | 6000 | 8500 |
| Notched Izod Impact | kJ/m² | 6 | 8 |
| Heat Deflection Temp (1.8 MPa) | °C | 205 | 215 |
| Density | g/cm³ | 1.45 | 1.53 |
| Mold Shrinkage | % | 0.3-0.8 | 0.2-0.6 |
4.Applications
1)Automotive – Engine covers, cooling fan blades, housings, brackets.
2) Electrical & Electronics – Coil bobbins, connectors, switches, sockets.
3)Industrial – Pump housings, gears, bearing cages, tool handles.
4)Consumer Goods – Power tool housings, kitchen appliance parts.
5.Processing Guide
Drying – 110-120°C for 3-4 hours (mandatory to avoid hydrolysis).
Melt Temperature – 240-270°C.
Mold Temperature – 60-100°C.
Injection Pressure – Medium to high.